Virat Aluminium

Size Range - 0.4mm to 800mm thickness

 

As per standards - EN573, EN485, ASTMB209

 

Chemical Symbols - EN AW-Al Cu4SiMg

 

High strength alloys with excellent machinability widely used in aircraft. Have limited formability and only fair corrosion resistance in the heat treated condition. Used for high strength parts in aircraft and machinery, including gears and bolts and for security vans where strength is critical.  

Specific applications include heavy duty forgings, plate, and extrusions for aerospace fittings, wheels, tanks, and major structural components, heavy duty automotive frame and suspension componentry. 2014 exhibits poor corrosion resistance for an aluminum alloy.

 

A high strength 4 to 5% Copper alloy produced in extruded bar and profile form, in the fully heat-treated condition (solution heat-treated & artificially aged). Normally stocked in the T651 condition (stress relieved by controlled stretching) Except for sizes under 10mm diameter and over 203.2mm diameter. (T6 only). Over 203.mm diameter is manufactured to chemical composition Only.

Machinability of aluminium alloy 2014A is very good.

 

Typical applications of aluminium alloy 2014A are high strength components especially for use in the aerospace and defence industries.

Additional Information:

• Delivery Time: Immediate
• Packaging Details: Plastic / Wooden Packing

Size Range - 5mm dia to 1000 mm dia

As per standards - EN573, EN755, ASTMB221-14, ASTMB211

Chemical Symbols - EN AW-Al Cu4SiMg

Aluminium Alloy 2014 is a copper-based alloy with very high strength plus excellent machining characteristics at some tempers. 2014 is often extruded and forged and it's one of the strongest aluminium alloys avaialble, being usually hard. It isn't great for welding because it tends to crack. It comes with poor resistance to corrosion, which is why it's often clad with pure aluminium. When unclad and used in a context where it's exposed to the weather, it needs a coat of paint to reduce the risk of corrosion.

Aluminium alloy 2014 is widely used in a variety of aerospace structural applications thanks to its very high strength. It's also used in manufacturing military vehicles, weapons, lorry frames, bridges, and structural projects. Other applications include heat treatment and annealing.

Additional Information:

• Delivery Time: Immediate
• Packaging Details: Plastic / Wooden Packing

Size Range - 5mm dia to 1000 mm diaAs per standards - EN573, EN755, ASTMB221-14, ASTMB211Chemical Symbols - EN AW-Al Cu4SiMg

 

Aluminium Alloy 2014 is a copper-based alloy with very high strength plus excellent machining characteristics at some tempers. 2014 is often extruded and forged and it's one of the strongest aluminium alloys avaialble, being usually hard. It isn't great for welding because it tends to crack. It comes with poor resistance to corrosion, which is why it's often clad with pure aluminium. When unclad and used in a context where it's exposed to the weather, it needs a coat of paint to reduce the risk of corrosion.

 

Aluminium alloy 2014 is widely used in a variety of aerospace structural applications thanks to its very high strength. It's also used in manufacturing military vehicles, weapons, lorry frames, bridges, and structural projects. Other applications include heat treatment and annealing.

Additional Information:

• Delivery Time: Immediate
• Packaging Details: Wooden / Plastic Packing

Size Range - 0.4mm to 800mm thickness

 

As per standards - EN573, EN485, ASTMB209

 

Chemical Symbols - EN AW-Al Cu4SiMg

 

High strength alloys with excellent machinability widely used in aircraft. Have limited formability and only fair corrosion resistance in the heat treated condition. Used for high strength parts in aircraft and machinery, including gears and bolts and for security vans where strength is critical.  

Specific applications include heavy duty forgings, plate, and extrusions for aerospace fittings, wheels, tanks, and major structural components, heavy duty automotive frame and suspension componentry. 2014 exhibits poor corrosion resistance for an aluminum alloy.

 

A high strength 4 to 5% Copper alloy produced in extruded bar and profile form, in the fully heat-treated condition (solution heat-treated & artificially aged). Normally stocked in the T651 condition (stress relieved by controlled stretching) Except for sizes under 10mm diameter and over 203.2mm diameter. (T6 only). Over 203.mm diameter is manufactured to chemical composition Only.

Machinability of aluminium alloy 2014A is very good.

 

Typical applications of aluminium alloy 2014A are high strength components especially for use in the aerospace and defence industries.

 

Additional Information:

• Delivery Time: Immediate
• Packaging Details: Plastic / Wooden Packing

Size Range - 5mm dia to 1000 mm diaAs per standards - EN573, EN755, ASTMB221-14, ASTMB211Chemical Symbols - EN AW-Al Cu4SiMg

 

Aluminium Alloy 2014 is a copper-based alloy with very high strength plus excellent machining characteristics at some tempers. 2014 is often extruded and forged and it's one of the strongest aluminium alloys avaialble, being usually hard. It isn't great for welding because it tends to crack. It comes with poor resistance to corrosion, which is why it's often clad with pure aluminium. When unclad and used in a context where it's exposed to the weather, it needs a coat of paint to reduce the risk of corrosion.

 

Aluminium alloy 2014 is widely used in a variety of aerospace structural applications thanks to its very high strength. It's also used in manufacturing military vehicles, weapons, lorry frames, bridges, and structural projects. Other applications include heat treatment and annealing.

Additional Information:

• Delivery Time: Immediate
• Packaging Details: plastic / wooden packing

Size Range - 5mm dia to 1000 mm diaAs per standards - EN573, EN755, ASTMB221-14, ASTMB211Chemical Symbols - EN AW-Al Cu4SiMg

 

Aluminium Alloy 2014 is a copper-based alloy with very high strength plus excellent machining characteristics at some tempers. 2014 is often extruded and forged and it's one of the strongest aluminium alloys avaialble, being usually hard. It isn't great for welding because it tends to crack. It comes with poor resistance to corrosion, which is why it's often clad with pure aluminium. When unclad and used in a context where it's exposed to the weather, it needs a coat of paint to reduce the risk of corrosion.

 

Aluminium alloy 2014 is widely used in a variety of aerospace structural applications thanks to its very high strength. It's also used in manufacturing military vehicles, weapons, lorry frames, bridges, and structural projects. Other applications include heat treatment and annealing.

Additional Information:

• Delivery Time: Immediate
• Packaging Details: Plastic / Wooden Packing

Size Range - 0.4mm to 800mm thickness

As per standards - EN573, EN485, ASTMB209

Chemical Symbols - EN AW-Al Cu4SiMg

High strength alloys with excellent machinability widely used in aircraft. Have limited formability and only fair corrosion resistance in the heat treated condition. Used for high strength parts in aircraft and machinery, including gears and bolts and for security vans where strength is critical.  

Specific applications include heavy duty forgings, plate, and extrusions for aerospace fittings, wheels, tanks, and major structural components, heavy duty automotive frame and suspension componentry. 2014 exhibits poor corrosion resistance for an aluminum alloy.

A high strength 4 to 5% Copper alloy produced in extruded bar and profile form, in the fully heat-treated condition (solution heat-treated & artificially aged). Normally stocked in the T651 condition (stress relieved by controlled stretching) Except for sizes under 10mm diameter and over 203.2mm diameter. (T6 only). Over 203.mm diameter is manufactured to chemical composition Only.

Machinability of aluminium alloy 2014A is very good.

Typical applications of aluminium alloy 2014A are high strength components especially for use in the aerospace and defence industries.

Additional Information:

• Delivery Time: Immediate
• Packaging Details: Plastic/ Wooden Packing

Size Range - 0.4mm to 800mm thickness

 

As per standards - EN573, EN485, ASTMB209

 

Chemical Symbols - EN AW-Al Cu4SiMg

 

High strength alloys with excellent machinability widely used in aircraft. Have limited formability and only fair corrosion resistance in the heat treated condition. Used for high strength parts in aircraft and machinery, including gears and bolts and for security vans where strength is critical.  

Specific applications include heavy duty forgings, plate, and extrusions for aerospace fittings, wheels, tanks, and major structural components, heavy duty automotive frame and suspension componentry. 2014 exhibits poor corrosion resistance for an aluminum alloy.

 

A high strength 4 to 5% Copper alloy produced in extruded bar and profile form, in the fully heat-treated condition (solution heat-treated & artificially aged). Normally stocked in the T651 condition (stress relieved by controlled stretching) Except for sizes under 10mm diameter and over 203.2mm diameter. (T6 only). Over 203.mm diameter is manufactured to chemical composition Only.

Machinability of aluminium alloy 2014A is very good.

 

Typical applications of aluminium alloy 2014A are high strength components especially for use in the aerospace and defence industries.

Additional Information:

• Delivery Time: Immediate
• Packaging Details: Plastic / Wooden Packing